Continuous Fiberglass Reinforced Thermoplastic CFRT UD tape prepreg for component
In short, what we could provide:
| 1 |
Continuous Fiberglass Reinforced Thermoplastic products, including
--Unidirectional tapes
--laminate
--sandwich panel
etc. |
| 2 |
Machinery line, which could produce the above products |
| 3 |
Factory construction guidance, from 0 to a functioning factory. |
Continuous glass fiber (GF) reinforced thermoplastic tape with unidirectional (UD) fiber orientation and a Polypropylene (PP) matrix in natural or black color.
Specification for Continuous glass fiber (GF) reinforced thermoplastic tape
| Fiber Types |
glass fiber, aramid fiber, carbon fiber |
| Resin Types |
Polypropylene (PP), Polyethylene (PE), Nylon (PA) |
| Tape Thickness |
0.15-0.4MM |
| Tape Areal Weight |
250gsm-620gsm |
| Tape Width |
0-650mm |
| Color |
natural and black, other colors can be customized |
| Glass Fiber content |
0%-70% by weight |
| Application |
Thermoplastic reinforced composite pipe, automotive parts, safety protection, wrapping cylinder, etc |
CFRT-UD Unidirectional belt
CFRT unidirectional tape is a single-layered, fiber-reinforced thermoplastic composite sheet in which the continuous fibers are unrolled and laid, and
impregnated with a thermoplastic resin. Fibers characterize it arranged parallel to each other (0° direction) without interlacing. Product width:
300mm/600mm/1200mm, can be customized.
Main applications: automotive interior and exterior trims, thermoplastic winding pipes, sports leisure, home building materials, transportation logistics, and aerospace.
Features of Thermoplastic Unidirectional Fiberglass Prepreg Tapes
Short fiber reinforced thermoplastic material: fiber length <1MM.
Long fiber reinforced thermoplastic material: fiber length 1 ~ 25MM.
Continuous Fiber Reinforced Thermoplastics: Length consistent with final product dimensions
The data sheet of Thermoplastic Unidirectional Tape PP GF 70-250 µm
Physical Properties
Glass Fibre Content 70 %wt
Fibre Areal Weight 290 g/m²
Fibre volume content 46 %
Prepreg Areal Weight 416 g/m²
Nominal Thickness 0,25 mm
Available Widths 3 mm to 300 mm
Thermal Properties
Melting Temperature 165 °C
Processing Temperature 180 - 220 °C
Mechanical Properties
Tensile Strength 940 MPa
Tensile Modulus 35 GPA
Flexural Strength 610 MPa
Flexural Modulus 34 GPA
For other ud tapes data sheets, contact us freely.
**Typical values are the average laboratory data, only for reference, not as a product standard.
The performance of continuous fiber-reinforced thermoplastic composites is very excellent. The longer the fiber length, the better the mechanical properties. Its specific strength can be more than 10 times that of ordinary steel. The higher the particular strength, the lighter the material used to achieve the corresponding strength. , so the continuous fiber-reinforced thermoplastic composite material can realize the real sense of replacing steel with plastic and lightweight applications.
The melt impregnation method is currently the most widely used and most industrialized method for manufacturing unidirectional belts. The process of the melt impregnation method is that the continuous fibers are fully impregnated with the molten thermoplastic resin through the process of yarn laying and yarn spreading, and through the impregnation mechanism.
Why us?
Good fiber dispersion:
The glass fiber is dispersed individually in the resin, which overcomes the problem of thermoplastic fiber dispersion.
Customized production:
using the melting process to meet different special performance requirements.
Mass production:
In mass production, the production cost is relatively low, and the quality is stable and reliable.